Scientific Reports volume 13, Article number: 2276 (2023) Cite this article

541 Accesses

3 Altmetric

Metrics details

This attempt has been made to synthesize the cellulose di-acetate in a solvent-free acetylation system of cotton Giza 86 cellulose with Ac2O (200 and 300 ml) in the presence of NiCl2.6HO (1.0, 1.5 and 2.0 g) as an effectively available and new catalyst by the conventional reflux and microwave irradiation methods. This study also illustrates the preparation of a dialysis membrane made from a cellulose di-acetate–dichloromethane-methanol-polyethylene glycol (MW: 200) casting solution. The microwave irradiation method for the synthesis of cellulose di-acetate showed excellent yields and short reaction time, which is an important feature of this method. The impact of the two methods on the cellulose di-acetate formation and its used in the dialysis membrane formulations was studied. The experimental degree of substitution of the prepared cellulose di-acetate values (DS = 2.00–2.7) showed an agreement with the calculated values by FTIR and 1H-NMR analysis methods. The formation of cellulose di-acetate with percentage yields varied from 62.85 to 89.85%. The applicability of the prepared membrane in dialysis operation was evaluated in terms of urea clearance, rejection of Bovine Serum Albumin (BSA) and flux of pure water. Characterization of cellulose di-acetate was achieved through 1H-NMR, FTIR, TGA, and BET analyses. The CA-PEG blend membrane was examined by contact angle measurement, porosity, and water uptake of the membrane. The cellulose acetate membrane surface morphology was determined using SEM. It is observable that the fabricated CA-PEG blend membrane from synthesized cellulose di-acetate by using Nickel chloride as a catalyst is showing remarkable rejection of BSA and urea clearance up to 100 and 67.2%, respectively. The present work is promising and applicable in dialysis membranes.

The evolution of solvent-free catalytic reaction, eco-friendly, economically viable, time of reaction and energy reduced methodology was becoming from our urgent demand to performance the chemical processes. The great importance of the esterification process in organic synthesis was attributed to the production of various useful organic compounds, such as polymers1,2. A great number of compounds in living organisms such as proteins, nucleic acids, and cellulose, have been made up of polymers. Moreover, polymers were the main constitutes of the minerals like diamond, quartz, and feldspar, as also as man-made materials as textiles, packaging, plastics, aircraft, construction and rope. Substantial investigation has been carried out in the esterification of cellulose, particularly solvent-free reactions and in the field of catalysis3,4,5. A variety of Lewis acids such as ZnCl26, CoCl27, and in particular, metal triflates such as Sc(OTf)38, Bi(OTf)29, Cu(OTf)210, and Sn(OTf)210 have been found to be operational catalysts for acylation. Also, NiCl2 was reported to be used as a catalyst to enhance the conversion and rate of acetylation of phenols, thiols, alcohols, and amines with Ac2O11. The reducing system of NiCl2 and NaBH4 efficiently produced the required (Z)-alkene-based-modified nucleotides, making NiCl2 a highly useful reagent to overcome some issues of over-reduction and/or breakdown12. Alonso et al.13,14,15 were synthesized the reducing agents consisting of NiCl2.2H2O, a catalytic amount of arene (naphthalene or 4,4′-di-tert-butylbiphenyl: DTTB) and excess powder of lithium. When nickel salts (1.5−2.5 equiv) and naphthalene (17 mol.%) were used, alkenes and alkynes were reduced into alkanes16,17. Similar to this, LiAlH4 (0.5–1.0 equiv) was also employed to accomplish a stereo- and regioselective hydroalumination of disubstituted acetylene in conjunction with a stoichiometric or catalytic quantity of low-valent transition metal halide NiCl218.

Several parameters constrained the conversion and reaction rate of the traditional esterification process. In the conventional esterification reaction, the reactants cannot be miscible, causing a slow kinetics communication between the reactants, so a thin film was formed and subsequently, the mass transfer was limited. To overcome these problems, the reaction is usually achieved by carrying out the reaction under supercritical conditions of high temperature and pressure with or without mixing, agitation, ultra-sonication, etc. In spite of the fact that, these methods were becoming highly efficient, but still cost serious and require high energy, making them uneconomic. The microwave heating method has recently been found to be an acceptable method for improving product yields and reaction rates in the synthetic chemical industry with extensive applications19.

The microwave treatment is regarded as a secure method for heating chemical mixtures to high temperatures because the energy of the microwave irradiation is transferred through electromagnetic waves and then results in a temperature that is higher than the medium's average temperature due to the interaction between molecules and microwave energy, which shortens reaction times and requires less energy than traditional heating methods by Motasemi and Ani20, and Buchori et al.21. However, high reaction temperatures were responsible for the high product yield under these circumstances. As it prevents catalyst contamination seen in other chemical processes, this method has been hailed as green, eco-friendly, safe, and reliable22. In the past ten years, several protocols for performing organic reactions, such as the acetylation of alcohols, phenols, thiols, amines, and cellulose in the absence of a solvent, have been reported. These protocols can also be accomplished using a microwave with excellent yields and correct times23,24,25.

A variety of polymers can be used to make dialysis membranes. The majority of these are applied polymers, polyacrylonitrile (PAN), including cellulose acetate (CA), polysulfone (PS), polymethyl methacrylate (PMMA), ethylene vinyl alcohol (EVAL) copolymer, and polyamide26. Recently, polymeric semi-permeable CA membranes have been widely used in hemodialysis therapy for patients’ renal failure to separate the protein and uremic toxins based on their molecular weights. The CA membranes have asymmetric structures27, solvent resistance, thermostability properties28, protein binding, minimizing fouling, good resistance to chlorine and solvent29,30, and are cheap and easily available31.

Polyvinyl alcohol (PVA) and polyethylene glycol (PEG) have been added to cellulose acetate hemodialysis membranes in order to improve their filtration capacity and biocompatibility32. Also, for this purpose33, was blending sericin with cellulose acetate to make cellulose acetate/sericin blend membranes to determine the efficiency's increment of CA membrane in the dialysis process. It is observable that the increase of 7.5% sericin in cellulose acetate remarkably enhances the rejection of BSA and urea clearance up to 96 and 60%, respectively. Polyaziridine or polyetyleneimine (PEI) are blended with CA to change the structure and performance efficiency to get the highest BSA rejection and urea clearance properties34. Based on urea and creatinine clearance, the effects of D-glucose monohydrate as an additive and formic acid (FA) as a solvent on the functionality of cellulose acetate dialysis membrane were examined35. The effect of different molecular weight PEG additives on cellulose acetate asymmetric dialysis membrane performance in urea clearance was studied36. By adding different quantities of monosodium glutamate (MSG) and formic acid, the permeability performance of cellulose acetate hemodialysis membranes was examined. The uremic toxins' increased permeability was caused by an increase in MSG concentration from 2 to 6 weight percent, which was a significant factor in determining the membrane morphologies37. Activated carbon (AC), zeolite (ZO), and graphene oxide (GO) were used to create porous cellulose acetate mixed-matrix membranes (MMMs). The potential to use them as hemoperfusion (HP) treatment units for the elimination of uremic toxins such p-cresol (PC) and creatinine (CRT) was investigated38.

This study aims to prepare cellulose di-acetate without solvents by acetylating cotton Giza 86 cellulose components using a novel catalyst NiCl2 utilizing conventional reflux and microwave irradiation methods. A dialysis membrane constructed of a casting solution of cellulose diacetate, dichloromethane, methanol, and polyethylene glycol (MW: 200) is also produced. 1H-NMR, FTIR, TGA, and BET studies were used to characterize the produced membrane and cellulose di-acetate. In expressions of urea clearance, pure water flow, and rejection of Bovine Serum Albumin (BSA) solution, the suitability of the produced membrane in dialysis operation is assessed.

The cotton Giza 86 was collected from Alexandria local market of Egypt. Sodium hydroxide, sodium hypochlorite, Ac2O and EtOH were supplied by Fluka analytical. Dichloromethane and methanol were obtained from (Sigma-Aldrich Co, Germany). Poly ethylene glycol (M.W. 200) was obtained from Acros-organic, USA. NiCl2.6H2O was received from Universal Fine chemicals PVT-LTD, India. Bovin serum albumin was supplied from (Biowest Co, USA). Urea Kits was used as purchased from Diamond Co, Germany.

To obtain the cellulose, the cotton Giza 86 was treated with 5 wt % sodium hydroxide solution with solid to liquid ratio of 1:10 (W/V) and heated in water bath at 70 °C for 2 h. The mixture was then filtered and washed with distilled water (dw) until the filtrate was clear. The bleaching process was performed via two steps, firstly, after alkali extraction, sodium hypochlorite (NaOCl) 2% solution was used at ratio of 1:10 (W/V) and heated in a water bath at 70 °C for 2 h, and the bleaching mixture was filtered and washed several times by dw. Bleaching step with NaOCl was repeated two times to purify the cellulose component. Secondly, the bleaching process was done with 5% H2O2 at a ratio of 1:10 (W/V) at 70 °C for 1 h. The mixture was filtered, washed several times by dw, squeezed and dried in an oven for 48 h at 50 °C.

20 g of extracted cotton Giza 86 cellulose, acetic anhydride (200 or 300 mL) and 2.0 g of NiCl2.6H2O as a green catalyst were combined in a 500 mL round bottom flask fitted with a condenser. The acetylation was performed under reflux at 140 °C for 48 h. After the reaction was complete, the reaction mixture was allowed to cool to room temperature before 100 mL of ethanol was added and thoroughly mixed in to break down the unreacted acetic anhydride. The product was then thoroughly cleaned with distilled water after being thoroughly washed in ethanol to remove any extra unneeded acetic acid and NiCl2 byproducts. The acetylated product was then dried for 24 h in an oven at 50 °C.

A mixture of Ac2O (200 mL), extracted cotton cellulose (20 g) and different weights of NiCl2 (1.0, 1.5, or 2.0 g) as a catalyst was placed into a Teflon cup (400 mL) and then put it into the microwave. The mixture was irradiated for 6, 8, or 10 min under an irradiation power of 1400 W. The Teflon cup was removed from the microwave once the reaction was complete and allowed to cool to room temperature. The Teflon cup's contents were transferred to a 500 mL beaker, and then they were mixed with 100 ml of ethanol for several minutes before filtering. The unreacted acetic acid and NiCl2 byproducts were then carefully rinsed from the product with distilled water. Samples were dried for 24 h in a 50 °C oven. The products were weighed in order to calculate the yield percentage and weight growth based on the starting dry cellulose. The difference between the product and starting weights was used to determine the weight increase.

The degree of substitution of the prepared cellulose acetates were measured experimentally and by FT-IR spectra and 1H NMR analyses1,2,3,4,5,24,25.

With the help of an Agilent Gel Permeation Chromatograph (GPC) using tetrahydrofuran as the solvent, the molecular weight, degree of polymerization, and polydispersity of cellulose acetate were all determined. A standard sample with a molecular weight range between 168 and 3,200,000 was used to calibrate the GPC apparatus.

The casting solution was prepared via dissolving of CA (22.5%) in 100 mL of dichloromethane and methanol (9:1) having a constant PEG (MW: 200) wt % of 0.5. To ensure that the polymers thoroughly mixed to create a homogenous solution, the casting solution temperature was maintained at 80 °C with 4 h of continuous stirring. Then, the casting solution was degassed by using the ultrasonic bath for 4 h to ensure no air bubbles were present. The casting solution was then spread over a dust-free glass plate using an Elcometer 4340 automatic film Application, UK with a 250 μm thickness at room temperature. The cast film was left on for 60 s in order to let the solvent evaporate and complete the phase inversion. The cast film was separated and washed for 30 min. at room temperature in a coagulation bath containing distilled water, inducing an exchange between the solvent and water. The cellulose acetate blend membrane was then transferred to a different container filled with distilled water and ethanol and stored at – 4 °C until it was ready for testing.

FTIR data for cellulose extracted from cotton Giza 86, all synthesized cellulose acetate, and CA-PEG blend membrane were obtained using Bruker VERTEX 70 spectrometer coupled to Platinum ATR unit in the range of 400–4000 cm−1. 1H-NMR for CA was obtained by 400 MHz Bruker Nuclear Magnetic Resonance Spectrometers and deuterated chloroform as a solvent. Utilizing the SDT650 Simultaneous Thermal Analyzer equipment, TGA measurements for cellulose, CA, and manufactured CA-PEG blend membrane were made in the range of 50 and 600 °C using a 5 °C/min ramp temperature underflow of high-quality N2 (100 mL/min) gas. The DSC/TG apparatus was calibrated before tests following the manufacturer's recommendations regarding weight, temperature, and DSC calibrations. Before each run, the instrument was also purged with air and a nitrogen flow for 10 min. By using the BELSORP mini-II, made by BEL Japan, INC, at 77 K as the adsorption temperature and saturated vapor pressure, measurements of the N2 adsorption–desorption isotherm under liquid nitrogen temperature were used to determine the specific surface area, pore volume, mean pore diameter, and mean particle size of the synthesized cellulose acetate and fabricated CA-PEG blend membrane. The samples were pre-treated at 120 °C with nitrogen gas flowing through them. The crystallinity and atomic or molecular structure of the synthesized CA and constructed CA-PEG mix membrane were examined using a Bruker D2 PHASER advance XRD analyzer. Using the SEM model JSM 6409A from JEOL, Japan, the surface and cross-section morphology of the manufactured CA-PEG blend membrane was examined.

The fabricated CA-PEG blend membrane was cut with an area of 12.57 cm2 and placed into the dead-end filtration test cell, which was occupied with 250 mL dw and exposed to the 1.0–2.0 bar pressure to performance the pure water permeation flux (PWP). The experiment was performed at room temperature as shown Fig. (1). The permeation flux of pure water (J) was measured from Eq. (1).

where J represents the permeation of pure water flux (L m–2 h–1), Q is the permeate solution volume (L), ∆t is the time of permeation (h), and A represents the testing membrane active area.

To define the hydrophobicity or hydrophilicity of the CA-PEG membrane, the contact angle was measured. A drop of water is placed on a material surface of fabricated CA-PEG blend membrane (4 cm2), and the drop forms a dome shape on the surface. The contact angle is the angle produced between the surface and the line perpendicular to the edge of the water drop (wetting angle), which measured by using Theta lite optical tensiometer with a digital video camera based optical tensiometer for measurement of static and surface tension of liquids by pendant drop method, Finland production.

To calculate the amount of water absorbed under specific circumstances, water absorption is utilized, so the performance of the prepared membrane in water or humid environment can be determined. For the water absorption test, a membrane sample of 4 cm2 was dried in an oven at a set temperature and time (12 h) before being put in a desiccator to cool. The membrane sample was weighted as soon as it had cooled. The membrane sample is subsequently submerged in a water under predetermined circumstances, frequently at 23 °C for 24 h. The sample of the membrane was taken out, dried with a lint-free cloth, and weighed. The membrane water absorption was determined using Eq. (2).

The dry–wet weight method can be used to determine the membrane porosity. The membrane porosity is calculated by using Eq. (3).

where WW (g) is the wet weight, DW is the membrane dry weight, Am (cm2) is the area of the membrane, DPW is the pure water density, and Tm (cm) is the membrane thickness.

The efficiency of dialysis membrane was determine in the terms of percent of BSA rejection by using the dead-end filtration test cell with effective membrane area of 12.57 cm2, and pressure 1.0–2.0 bar at room temperature, as shown in Fig. 1. The concentration of BSA solution used was 1.0 mg/mL. The concentration of BSA in permeate was analyzed by measuring its absorbance with spectrophotometer (Digital a spectrophotometer (Analytic Jena—SPEKOL1300 UV/Visible spectrophotometer) matched with glass cells of 1 cm optical path) at a wavelength of λ550 nm using the Biuret Reagent39. The rejection of BSA of fabricated CA-PEG blend membrane was determined by Eq. (4).

Schematic Figure of dead-end filtration cell for water flux and BSA rejection.

The urea clearance was determined for the fabricated CA-PEG blend membrane. The concentration of urea solution was 50 mL of 1 mg/mL which placed into the donor side and about 2 L distilled water was poured onto the receiver side as shown in Fig. 2. The changing in concentration of urea on donor and receiver sides was measured using enzymatic colorimetric method after every 30 min for 210 min. The concentration of urea was determined by measuring its absorbance with a spectrophotometer at a wavelength of λ578 nm. The concentration of urea was calculated by using Eq. (5).

Schematic figure of dialysis cell for urea clearance.

where C0 is the initial concentration at time zero, Ct is the final concentration at time t, and UC% is the urea clearance.

This work is concerned with the preparation of cellulose di-acetate from cotton Giza 86 cellulose, which is convenient for the preparation of dialysis membrane by using a novel Lewis acid catalyst like NiCl2.6H2O and compared between the convention and microwave methods for the acetylation of cellulose. In the conventional method, the effect of amount of acetic anhydride used was only investigated. As shown in Table 1, 20.0 g of cellulose extracted from cotton Giza 86 was refluxed at 140 °C in about 200 mL (Ac2O) (Sample 1) and in acetic anhydride (300 mL) (Sample 2) in the existence of 2.0 g of NiCl2.6H2O for 48 h. The previous reactions showed that the % yields of CA were 86.25% (DS = 2.59, Sample 1) and 81.74% (DS = 2.45, Sample 2) with increasing the amount of acetic anhydride from 200 to 300 mL, respectively. So, it has been chosen 200 mL of Ac2O and 20 g of cellulose extracted from cotton Giza 86 for acetylation under microwave as an optimum amount. To achieve the targeted DS and control the acetylation reaction conditions, the reaction was repeated under microwave irradiation conditions, changing only the amount of catalyst and reaction time. As reported in Table 1, when the amount of NiCl2.6H2O is 1.0 g, the reaction was performed just after 6 min with a high % yield of 88.30% (31.30 g, DS = 2.63, Sample 3). When the reaction time was extended to 8 min, there was very little change in yields (31.90 g, DS = 2.70, Sample 4) with a percentage yield of 89.85%. While when this reaction was performed for 10 min, the product started to be affected by the time and began to be hydrolysis, so there was a little decrease in the yield (31.20 g, DS = 2.64, 87.94% Sample 5). As shown in Table 1, when the amount of NiCl2.6H2O increased to 1.5 g, the yield was highly decreased to about 23.16, 23.30 and 23.16 g for 6, and 10 min reaction time (DS = 2.0, Samples 6, 7, and 8, respectively). From the previous results, the excess of the quantity of catalyst to 1.5 g was greatly affected the targeted DS values, which became undesirable values (DS ~ 2.6) for the preparation of the dialysis membrane. When increased the quantity of NiCl2.6H2O to 2.0 g as reported in the above-mentioned convention method but under microwave conditions, the product yields were 28.24 g at 6 min, 31.15 g at 8 min, and 24.34 g at 10 min (Table 1). From previous experiments, it can be concluded that, 1.0 g of NiCl2.6H2O as a catalyst using the microwave irradiation method is sufficient to produce cellulose di-acetate with a percentage yield of 89.85% in 8 min in the presence of 200 mL of Ac2O.

All the products (Samples 1–11) were examined by FT-IR analysis, and the degree of substitution (DS) was calculated experimentally and by using FT-IR, the results referred to a successful formation of cellulose di-acetate with different % yields, but also, with a very little variation on DS values (Table 1). The weight gain was also calculated using FT-IR (Table 1). Firstly Sample 5, which has a DS = 2.64 was chosen as a start material for the fabricated CA-PEG blend membrane after testing most prepared cellulose di-acetate samples. Figure 3 displays the FT-IR spectra of cellulose extracted from cotton Giz-86, Sample 5 as a pure cellulose di-acetate and fabricated CA-PEG blend membrane. The FT-IR spectra for the cellulose extracted from cotton Giza 86 displays strong broadband at 3334.81 cm–1 due to the stretching –OH, a small band at 2894.73 cm–1 ascribed to the stretching mode of –CH, and two bands were greatly decreased in cellulose di-acetate (Sample 5) and in fabricated CA-PEG blend membrane, which proved the successfully performed of cellulose acetylation. Figure 3 shows no chemical change occurred for the pure cellulose di-acetate (Sample 5) in the functionalizing group during blending, except a small shifting was noticed. Figure 3 shows the appearance of strong sharp peaks at 1743.25 and 1739.22 cm–1 due to C = O for Sample 5 and CA-PEG blend membrane, respectively. Compared CA (Sample 5) and CA-PEG blend membrane, the absorption peaks appeared sharply at 1370.81 and 1369.39 cm−1 due to the acetyl group C–H bending band. A strong sharper peak slightly shifted from 1224.01 in Sample 5 to 1215.11 cm−1 in CA-PEG blend membrane, which was assigned to the ester C–O stretching band. The peaks at 1040.23 and 1033.56 cm−1 belonging to the pyranose ring C–O–C asymmetric stretching were reported for Sample 5 and CA-PEG blend membrane, respectively.

FTIR analysis of (a) Cellulose extracted from cotton Giza 86, (b) Cellulose di-acetate (Sample-5), (c) CA-PEG blend membrane prepared from Sample 5.

The DS of cellulose di-acetate (Sample 5) was measured also by using 1H- NMR spectra. Figure 4 displays the 1H-NMR spectrum of Sample 5 with a DS value of almost 2.66 demonstrating the creation of cellulose di-acetate using NiCl2.6H2O and microwave irradiation.

1H-NMR spectrum of Sample 5.

The gel permeation chromatography (GPC) was used to calculate the molecular weight, degree of polymerization, and the polydispersity index of a cellulose acetate (Sample 5) as shown in Fig. 5. From the results, the degree of polymerization was about 149, weight average molecular weight (Mw) was 38,362 (g/mol), number average molecular weight (Mn) was 5864 (g/mol), z average molecular weight (Mz) was 339,278 (g/mol), viscosity average molecular weight (Mv) was 273,659 (g/mol), molecular weight at peak maximum of the elugram (Mp) was 18,098 (g/mol), and the polydispersity index (PD) was 6.542.

The gel permeation chromatography (GPC) analysis of cellulose di-acetate (Sample 5).

Thermo gravimetrical analysis (TGA) is a realistic characterization technique for evaluating the thermal stability of specific materials. The TGA thermal curves of the CA (Sample 5) and fabricated CA-PEG blend membrane are exposed in Fig. 6a,b at a heating rate 5 °C/min. TGA of cellulose di-acetate (Sample 5) (Fig. 6a) shows decomposition occurring via one step and 84.06% weight loss between 327.13 and 600 °C with the maximum decomposition occurring at 356.84 °C. TGA of fabricated CA-PEG blend membrane (Fig. 6b) shows decomposition occurring via two steps. The first weight loss (81.02%) was occurred between 327.13 and 400 °C with the maximum decomposition occurring at 347.91 °C, while the second weight loss (10.42%) was happened between 400 and 600 °C with the maximum decomposition happening at 560.0 °C.

TGA analysis of (a) Cellulose di-acetate (Sample 5), (b) CA-PEG blend membrane from cellulose di-acetate (Sample 5) and PEG.

BET can produce reliable precision measurement data for the adsorption amount of adsorptive material relative to the pressure. Figure 7a shows the adsorption/desorption isotherm of fabricated CA-PEG blend membrane and also explains the relation between the relative pressure (p/p0) and specific amount adsorbed (Va: cm3 (STP) g–1). The results from the Fig. 7b showed that, the adsorption isotherm type may be measured as mixed types of III and V. The monolayer volume (Vm) was 5.9709 cm3 (STP) g–1, BET specific surface area (asBET) was 25.9880 m2 g–1, energy constant of the first layer (C) was 0.6296, total pore volume (p/p0) was 0.00909 cm3 g–1 and the mean pore diameter was 1.3993 nm. According to the above-mentioned results, it can be deduced that the fabricated CA-PEG blend membrane is porous with micropores40,41,42,43.

Surface area analysis (a) Adsorption/desorption isotherm, (b) BET analysis plot, (c) Micropore analysis (MP) plot.

The MP-plot is convenient for defining the presence or absence of micropores and their range of size40,41,42,43. From the Fig. 7c, it can be deduced that the fabricated CA-PEG blend membrane has micropores diameter (dp) of 0.7 to 0.9 nm with a distribution peak at 0.8 nm. Also, it has micropores diameter of 1.1 to 1.25, 1.25 to 1.4, 1.4 to 1.55 and 1.6 to 1.8 nm with distribution peaks at 1.2, 1.3, 1.5 and 1.7 nm, respectively. The total specific surface area (a1) was 0.5349) m2 g–1, the external specific surface area (a2) was 5.4092 m2 g–1, and the pore volume (Vp) was 0.0009 cm3 g–1.

The XRD analysis was used to confirm the occurrence of a targeted successful acetylation process. It is known that the attendance of the acetyl groups in cellulose increased the hydrophobicity and increased the hydrophobicity of the prepared membrane. The patterns of cellulose extracted from cotton Giza 86, the cellulose acetate (Sample 5) and the fabricated CA-PEG blend membrane are compared in Fig. 8a,b,c. Figure 8a gave X–ray patterns with major peaks at 14.7°(Iα (100) or Iβ (110)), 16.4° (Iα (010) or Iβ (110)), 22.8° (Iα (110) or Iβ (200)) and 34.4° ((Iα and Iβ (400)), reflections for cellulose extracted from cotton Giza 86, which may be belongs to the Iα or Iβ predominant. The Z function Eq. (6) was used to determine the conformation of the chiral carbon of cellulose.

XRD analysis of (a) Cellulose extracted from cotton Giza 86, (b) Cellulose di-acetate, (c) CA-PEG blend membrane.

The d1 was found to be 6.005 nm (d-spacing of peak at 14.7°), d2 was 16.504 nm (d-spacing of the peak at 16.4° (2θ), and Z value was –5268.474. From the negative Z-value of cellulose extracted from cotton Giza 86, it can be deduced that the extracted cellulose compound has Iβ dominant form44. Figure 8b,c gave X–ray patterns of the cellulose acetate (Sample 5) and the fabricated CA-PEG blend membrane with the same previous major peaks, but the relative height of intensity of diffraction peaks was decreased while the amorphous region increased. Also, there was a broadening in diffraction peaks occurred. The degree of crystallinity of the cellulose sample was considered to be 45.6%, the cellulose acetate (Sample 5) was 22.5% while in the fabricated CA-PEG blend membrane was 15.2%, which indicated a decrease in the crystallinity degree after esterification. This decrease in crystallinity in cellulose acetate (Sample 5) and the fabricated CA-PEG blend membrane compared with the cellulose sample could be due to the replacement of the hydroxyl groups by acetyl groups with a larger volume. During acetylation, the acetyl group was causing the breaking of inter- and intramolecular hydrogen bonds of cellulose, leading to the degradation in the crystal structure of cellulose. This result confirmed why the cellulose acetate (Sample 5) and the fabricated CA-PEG blend membrane are highly amorphous45. Also, Fig. 8b,c showed a remarkable peak at 7.9° (2θ) assigned to semicrystalline acetylated cellulose. This result was attributed to the presence of acetyl groups which caused an increase in the interfibrillar distance of the cellulose chains46,47.

Figure 9 shows the SEM surface and cross-sectional morphology of the fabricated CA-PEG blend membrane. From Fig. 9, the creation of an asymmetric membrane with nano-sized pores can be clearly viewed. The blending of PEG with cellulose acetate during the casting process improved the phase inversion mechanism.

SEM analysis of CA-PEG blend membrane (a) Surface morphology, and (b) Cross-sectional morphology.

Water absorption measurement was used to define the hydrophobicity and hydrophilicity of the prepared membrane. According to Eq. (2), the percentage of water absorption of fabricated CA-PEG blend membrane was found to be 2.91%. The very lowering value of water absorption measurement indicated that the fabricated CA-PEG blend membrane is highly hydrophobic.

The contact angle was also used to characterize the hydrophobicity and hydrophilicity of the membrane, it is known that a high contact angle value usually means high hydrophobicity. The fabricated CA-PEG blend membrane showed that, the value of the contact angle was 92.5 degree. The increment of contact angle value means, the fabricated CA-PEG blend membrane is highly hydrophobic48,49.

The porosity of the fabricated CA-PEG blend membrane was calculated according to Eq. (3), and it was found to be 1.22%. The membrane porosity was enhanced when the PEG was blending with cellulose acetate. This value indicated that the fabricated membrane could be used for an ultrafiltration application (0.1–10%)50.

The flux of pure water is the most parameter used to measure the hydraulic permeability of the membrane in micro, dialysis and ultrafiltration membranes. The flux of Pure water of fabricated CA-PEG blend membrane was calculated by the dead-end filtration test cell according to Eq. (3) by determining the amount of the pure collecting water (0.078 L) through a certain time (3.5 h) under a certain pressure (1.0–2.0 bar)51,52,53,54. Distilled water is used as the feed in the flux performance experiment. In fabricated CA-PEG blend membrane, the pure water permeation flux (PWP) value at the operating pressure (1.0–2.0 bar) was 17.73 L/m2∙h. From this value, we can deduced that the water flux performance of the fabricated CA-PEG blend membrane from synthesized cellulose di-acetate (Sample 5) by using NiCl2 as a catalyst was convenient to use in the dialysis process51,52,53,54.

Bovine serum albumin has an important role during the formation of calcium oxalate crystals which prevents the nucleation of calcium oxalate, so the urine stone will not be formed. From the view of the importance of bovine serum albumin, it is necessary not to lose the patient BSA during the dialysis process. The result in terms of BSA rejection indicates that the fabricated CA-PEG blend membrane from synthesized cellulose di-acetate (Sample 5) can retain all of the BSA successfully and with the highest rate of 100%55,56.

Urea clearance is important to assess kidney functions, so urea clearance should be measured. Urea clearance was the amount of blood or plasma cleared by the kidneys from urea within minutes. According to Eq. (5), urea clearance percentage was 67.2% after 2.5 h for the fabricated CA-PEG blend membrane from synthesized cellulose di-acetate (Sample 5). All the above-mentioned results proved the applicability of the fabricated CA-PEG blend membrane for dialysis57,58,59.

Synthesis of the cellulose di-acetate using a solvent-free acetylation system from cellulose extracted from cotton Giza 86 by investigation of 200 and 300 mL Ac2O in the existence of NiCl2.6HO (1.0, 1.5 and 2.0 g) as a new catalyst was completed using the conventional reflux and the microwave irradiation methods. The prepared cellulose di-acetate was tested for the fabrication of PEG blend membrane. The fabricated CA-PEG blend membrane was also tested for dialysis application. The preparation of cellulose di-acetate using the microwave irradiation method showed excellent yields and short reaction time, which makes the proposed method important for commercial trial. The impact of the two methods used on the formation of cellulose di-acetate and its use in the dialysis membrane formulations was studied. The experimental degree of substitution of the prepared cellulose di-acetate values was in agreement with that calculated by FTIR and 1H-NMR analysis methods. The fabricated membrane was found to be applicable in the dialysis operation regarding urea clearance, pure water flux and rejection of Bovine Serum Albumin (BSA). Certainly, the present work is promising and applicable in dialysis membranes.

The datasets used in this investigation are accessible for review upon request from the corresponding author of the paper.

Activated carbon

Cellulose acetate

Acetic anhydride

BET specific surface area

Brunauer–Emmett–Teller

Bismuth(III) trifluoromethanesulfonate

Bovine Serum Albumin

Energy constant of the first layer

Cellulose acetate-polyethylene glycol

Cobalt chloride

Creatinine

Copper(II) trifluoromethanesulfonate

Degree of polymerization

Micropores diameter

Degree of substitution

4,4′-Di-tert-butylbiphenyl

Distilled water

Ethanol

Ethylene vinyl alcohol

Formic acid

Fourier-transform infrared spectroscopy

Graphene oxide

Gel Permeation Chromatograph

Hydrogen peroxide

Hemoperfusion

Lithium aluminum hydride

Mixed-matrix membranes

Number average molecular weight

Micropore

Molecular weight at peak maximum of the elugram

Monosodium glutamate

Viscosity average molecular weight

Molecular weight

Average molecular weight

Sodium borohydride

Sodium hypochlorite

Nickel chloride six hydrate

Nuclear magnetic resonance

Polyacrylonitrile

P-cresol

Polydispersity index

Polyethylene glycol

Polyetyleneimine

Polymethyl methacrylate

Polysulfone

Polyvinyl alcohol

Pure water permeation flux

Scandium(III) triflate

Scanning electron microscope

Tin(II) trifluoromethanesulfonate

Thermo gravimetrical analysis

Monolayer volume

Pore volume

Total pore volume

Weight gain

X-ray diffraction analysis

Zink chloride

Zeolite

El Nemr, A., Ragab, S., El Sikaily, A. & Khaled, A. Synthesis of cellulose triacetate from cotton cellulose by using NIS as a catalyst under mild reaction conditions. Carbohydr. Polym. 130, 41–48. https://doi.org/10.1016/j.carbpol.2015.04.065 (2015).

Article CAS Google Scholar

El Nemr, A., Ragab, S. & El Sikaily, A. Rapid synthesis of cellulose triacetate from cotton cellulose and its effect on specific surface area and particle size distribution. Iran. Polym. J. 26(4), 261–272. https://doi.org/10.1007/s13726-017-0516-2 (2017).

Article CAS Google Scholar

Ragab, S., Eleryan, A. & El Nemr, A. Ferric perchlorate hydrate as a new catalyst for highly efficient esterification of cellulose at room temperature. Sci. Rep. 12, 5643. https://doi.org/10.1038/s41598-022-09669-w (2022).

Article ADS CAS Google Scholar

Ragab, S. & El Nemr, A. Zirconyl chloride as a novel and efficient green Lewis acid catalyst for direct acetylation of cotton cellulose in the presence and absence of solvent. J. Polym. Res. 26, 156. https://doi.org/10.1007/s10965-019-1816-3 (2019).

Article CAS Google Scholar

El Nemr, A. & Ragab, S. Acetylation of Cotton-Giza 86 cellulose using MnCl2 as a new catalyst and its application to machine oil removal. Environ. 5(4), 895–905. https://doi.org/10.1007/s40710-018-0330-7 (2018).

Article Google Scholar

Baker, R. H. & Bordwell, F. G. Organic Syntheses Vol. 3, 141 (Wiley, New York, 1955).

Google Scholar

Iqbal, J. & Srivastava, R. R. Cobalt (II) chloride catalyzed acylation of alcohols with acetic anhydride: Scope and mechanism. J. Org. Chem. 57(7), 2001–2007. https://doi.org/10.1021/jo00033a020 (1992).

Article CAS Google Scholar

Ishihara, K., Kubota, M., Kurihara, H. & Yamamoto, H. Scandium trifluoromethanesulfonate as an extremely active Lewis acid catalyst in acylation of alcohols with acid anhydrides and mixed anhydrides. J. Org. Chem. 61(14), 4560–4567. https://doi.org/10.1021/jo952237x (1996).

Article CAS Google Scholar

Orita, A., Tanahashi, C., Kakuda, A. & Otera, J. Highly powerful and practical acylation of alcohols with acid anhydride catalyzed by Bi(OTf)3. J. Org. Chem. 66(26), 8926–8934. https://doi.org/10.1021/jo0107453 (2001).

Article CAS Google Scholar

Chandra, K. L., Saravanan, P., Singh, R. K. & Singh, V. K. Lewis acid catalyzed acylation reactions: Scope and limitations. Tetrahedron 58(7), 1369–1374. https://doi.org/10.1016/S0040-4020(01)01229-7 (2002).

Article CAS Google Scholar

Meshram, G. & Patil, V. D. Simple and efficient method for acetylation of alcohols, phenols, amines, and thiols using anhydrous NiCl2 under solvent-free conditions. Synth. Commun. 39, 4384–4395. https://doi.org/10.1080/00397910902906529 (2009).

Article CAS Google Scholar

Lee, S. E., Vyle, J. S., Williams, D. M. & Grasby, J. A. Novel syntheses of (Z)-alkene and alkane base-modified nucleosides. Tetrahedron Lett. 41(2), 267–270. https://doi.org/10.1016/S0040-4039(99)02029-8 (2000).

Article CAS Google Scholar

Alonso, F., Radivoy, G. & Yus, M. Active nickel-based reduction of organic compounds. Russ. Chem. Bull. 52(12), 2563–2576. https://doi.org/10.1023/B:RUCB.0000019874.01782.b4 (2003).

Article CAS Google Scholar

Alonso, F. & Yus, M. The NiCl2–Li–arene (cat.) combination: A versatile reducing mixture. Chem. Soc. Rev. 33(5), 284–293. https://doi.org/10.1039/B315131J (2004).

Article CAS Google Scholar

Alonso, F., Riente, P. & Yus, M. Nickel nanoparticles in hydrogen transfer reactions. Acc. Chem. Res. 44(5), 379–391. https://doi.org/10.1021/ar1001582 (2011).

Article CAS Google Scholar

Alonso, F. & Yus, M. Hydrogenation of olefins with hydrated nickel chloride, lithium and a catalytic amount of naphthalene. Tetrahedron Lett. 37(38), 6925–6928. https://doi.org/10.1016/0040-4039(96)01518-3 (1996).

Article CAS Google Scholar

Alonso, F. & Yus, M. Hydrogenation of alkynes with hydrated nickel chloride, lithium and a catalytic amount of naphthalene. Tetrahedron Lett. 38(1), 149–152. https://doi.org/10.1016/S0040-4039(96)02239-3 (1997).

Article CAS Google Scholar

Ibragimov, A. G., Ramazanov, I. R., Khalilov, L. M., Sultanov, R. M. & Dzhemilev, U. M. Regio-and stereo-selective hydroalumination of disubstituted acetylenes with Et3Al catalysed by (η5-C5H5) 2TiCl2. Mendeleev Commun. 6(6), 231–232. https://doi.org/10.1016/S0959-9436(96)71434-7 (1996).

Article Google Scholar

Loupy, A. & Varma, R. S. Microwave effects in organic synthesis. Chim. Oggi–Chem. Today. 24(3), 36. https://doi.org/10.1002/chin.200720275 (2006).

Article CAS Google Scholar

Motasemi, F. & Ani, F. N. A review on microwave-assisted production of biodiesel. Renew. Sustain. Energy Rev. 16(7), 4719–4733. https://doi.org/10.1016/j.rser.2012.03.069 (2012).

Article CAS Google Scholar

Buchori, L., Istadi, I. & Purwanto, P. Advanced chemical reactor technologies for biodiesel production from vegetable oils—A review. Bull. Chem. React. Eng. 11(3), 406–430. https://doi.org/10.9767/bcrec.11.3.490.406-430 (2016).

Article CAS Google Scholar

Nguyen, H. C., Ong, H. C., Pham, T. T. T., Dinh, T. K. K. & Su, C.-H. Microwave mediated noncatalytic synthesis of ethyl levulinate: A green process for fuel additive production. Int. J. Energy. Res. 44, 1698–1708. https://doi.org/10.1002/er.4985 (2020).

Article CAS Google Scholar

Constantinou-Kokotou, V. & Peristeraki, A. Microwave-assisted NiCl2 promoted acylation of alcohols. Synth. Commun. 34(22), 4227–4232. https://doi.org/10.1081/SCC-200036636 (2004).

Article CAS Google Scholar

El Nemr, A., Ragab, S. & El Sikaily, A. Testing zinc chloride as a new catalyst for direct synthesis of cellulose di-and tri-acetate in a solvent free system under microwave irradiation. Carbohydr. Polym. 151, 1058–1067. https://doi.org/10.1016/j.carbpol.2016.06.072 (2016).

Article CAS Google Scholar

Ragab, S. & El Nemr, A. Nanofiber cellulose di- and tri-acetate using ferric chloride as a catalyst promoting highly efficient synthesis under microwave irradiation. J. Macromol. Sci. Pure Appl. Chem. 55, 124–134. https://doi.org/10.1080/10601325.2017.1387741 (2017).

Article CAS Google Scholar

Deshmukh, S. P. & Li, K. Effect of ethanol composition in water coagulation bath on morphology of PVDF hollow fiber membrane. J. Membr. Sci. 150, 75–85. https://doi.org/10.1016/S0376-7388(98)00196-3 (1998).

Article CAS Google Scholar

Loeb, S. & Sourirajan, S. Sea water demineralization by means of an osmotic membrane. Adv. Chem. Ser. 38, 117. https://doi.org/10.1021/ba-1963-0038.ch009 (1963).

Article CAS Google Scholar

Chen, Y. et al. Characterization of regenerated cellulose acetate. Chin. J. Polym. Sci. 20, 369–375. https://doi.org/10.1016/j.carbpol.2017.03.057 (2002).

Article CAS Google Scholar

Combe, C., Molis, E., Lucas, P., Riley, R. & Clark, M. M. The effect of CA membrane properties on adsorptive fouling by humic acid. J. Membr. Sci. 154, 73–87. https://doi.org/10.1016/S0376-7388(98)00268-3 (1999).

Article CAS Google Scholar

Chaudry, M. A. Water and ions transport mechanism in hyperfiltration with symmetric cellulose acetate membranes. J. Membr. Sci. 206, 319–332. https://doi.org/10.1016/S0376-7388(01)00783-9 (2002) (Get rights and content).

Article CAS Google Scholar

Yin, L., Huanlin, C., & Bogeng, L. Influence of additives on phase separation process of PVDF solution and membrane morphology. Acta Polym Sin. 5, 656–661 (2002). https://doi.org/WOS:000178936800021

Azhar, O. et al. Cellulose acetate-polyvinyl alcohol blend hemodialysis membranes integrated with dialysis performance and high biocompatibility. Mater. Sci. Eng. 126, 112127. https://doi.org/10.1016/j.msec.2021.112127 (2021).

Article CAS Google Scholar

Waheed, H., Minhas, F. T. & Hussain, A. Cellulose acetate/sericin blend membranes for use in dialysis. Polym. Bull. 75, 3935–3950. https://doi.org/10.1007/s00289-017-2238-1 (2018).

Article CAS Google Scholar

Waheed, H. & Hussain, A. Fabrication of cellulose acetate/polyaziridine blended flat sheet membranes for dialysis application. Bio Nanosci. 9, 256–265. https://doi.org/10.1007/s12668-019-0600-5 (2019).

Article Google Scholar

Idris, A., Yee, H. K. & Kee, C. M. Preparation of cellulose acetate dialysis membrane using D-glucose monohydrate as additive. J. Teknol. 51(1), 67–76. https://doi.org/10.11113/jt.v51.147 (2009).

Article Google Scholar

Idris, A. & Lee, K. Y. The effect of different molecular weight PEG additives on cellulose acetate asymmetric dialysis membrane performance. J. Membr. Sci. 280, 920–927. https://doi.org/10.1016/j.memsci.2006.03.010 (2006).

Article CAS Google Scholar

Kee, C. M. & Idris, A. Permeability performance of different molecular weight cellulose acetate hemodialysis membrane. Sep. Purif. Technol. 75, 102–113. https://doi.org/10.1016/j.seppur.2010.08.013 (2010).

Article CAS Google Scholar

Hsiao, Y.-S. et al. Porous cellulose acetate mixed-matrix membrane adsorbents for efficient clearance of p-cresol and creatinine from synthetic serum. J. Taiwan. Inst. Chem. Eng. 133, 104199. https://doi.org/10.1016/j.jtice.2021.104199 (2022).

Article CAS Google Scholar

Gornall, A. G., Bardawill, C. J. & David, M. M. Determination of serum proteins by means of the biuret reaction. J. Biol. Chem. 177(2), 751–766. https://doi.org/10.1016/S0021-9258(18)57021-6 (1949).

Article CAS Google Scholar

Rouquerol, F., Rouquerol, J. & Sing, K. S. W. Adsorption by powders and porous solids (Academic Press INC., 1999).

Google Scholar

Gregg, S. J. & Sing, K. S. W. Adsorption surface area and porosity 2nd edn. (Academic Press INC., 1982).

Google Scholar

Brunauer, S., Emmett, P. H. & Teller, E. Adsorption of gases in multimolecular layers. J. Am. Chem. Soc. 60, 309 (1938).

Article ADS CAS Google Scholar

Barrett, E. P., Joyner, L. G. & Halenda, P. P. The determination of pore volume and area distributions in porous substances I. Computations from nitrogen isotherms. J. Am. Chem. Soc. 73, 373 (1951).

Article CAS Google Scholar

Hult, E. L., Iversen, T. & Sugiyama, J. Characterization of the supermolecular structure of cellulose in wood pulp fibres. Cellulose 10, 103–110. https://doi.org/10.1023/A:1024080700873 (2003).

Article CAS Google Scholar

Nabili, A., Fattoum, A., Christine, M., Salon, B. & Bras, J. Synthesis of cellulose triacetate-I from microfibrillated date seeds cellulose (Phoenix dactylifera L.), Elimame Elaloui1. Iran. Polym. J. 26, 137–147. https://doi.org/10.1007/s13726-017-0505-5 (2017).

Article CAS Google Scholar

Hu, W., Chen, S., Xu, Q. & Wang, H. Solvent-free acetylation of bacterial cellulose under moderate conditions. Carbohyd Polym. 83, 1575–1581. https://doi.org/10.1016/j.carbpol.2010.10.016 (2011).

Article CAS Google Scholar

Zepic, V., Poljanšek, I., Oven, P., Škapin, A. S. & Hancic, A. Effect of drying pretreatment on the acetylation of nanofibrillated cellulose. BioResources 10, 8148–8167. https://doi.org/10.15376/BIORES.10.4 (2015).

Article CAS Google Scholar

Nurkhamidah, S. et al. Enhancing properties and performance of cellulose acetate/polyethylene glycol (CA/PEG) membrane with the addition of titanium dioxide (TiO2) by using surface coating method. MATEC Web Conf. 156, 08016. https://doi.org/10.1051/matecconf/201815608016 (2018).

Article CAS Google Scholar

Jayalakshmi, A., Kim, I.-C. & Kwon, Y.-N. Cellulose acetate graft-(glycidylmethacrylate-g-PEG) for modification of AMC ultrafiltration membranes to mitigate organic fouling. RSC Adv. 5, 48290–48300. https://doi.org/10.1039/C5RA03499J (2015).

Article ADS CAS Google Scholar

Cuperus, F. P. & Smolders, C. A. Characterization of UF membranes membrane characteristics and characterization techniques. Adv. Colloid Interface Sci. 34, 135–173. https://doi.org/10.1016/0001-8686(91)80049-P (1991).

Article CAS Google Scholar

Singh, R. Membrane technology and engineering for water purification: application, systems design and operation (Butterworth-Heinemann, 2014).

Google Scholar

Jagschies, G. et al. (eds) Biopharmaceutical processing: development, design, and implementation of manufacturing processes (Elsevier, 2018). https://doi.org/10.1016/C2014-0-01092-1.

Book Google Scholar

Luis, P. Fundamental Modeling of Membrane Systems: Membrane and Process Performance. ISBN: 978-0-12-813483-2. (Elsevier Ltd, 2018). https://doi.org/10.1016/C2016-0-02489-0

Basile, A., & Nunes, S. P. (Eds.). Advanced Membrane Science and Technology for Sustainable Energy and Environmental Applications (2011).

Aronson, J.K., DPhil, M.A., FRCP, M.B.Ch.B., HonFFPM, HonFBPhS, Bovine serum albumin. in Meyler's Side Effects of Drugs, 1045–1045. 16th edn (Elsevier B.V., 2016)

Jahanban-Esfahlan, A. et al. Recent developments in the detection of bovine serum albumin. Int. J. Biol. Macromol. 138, 602–617. https://doi.org/10.1016/j.ijbiomac.2019.07.096 (2019).

Article CAS Google Scholar

Farnebo, S., Samuelsson, A., Henriksson, J., Karlander, L.-E. & Sjöberg, F. Urea clearance: A new method to register local changes in blood flow in rat skeletal muscle based on microdialysis. Clin. Physiol. Funct. Imaging 30(1), 57–63. https://doi.org/10.1111/j.1475-097X.2009.00904.x (2010).

Article CAS Google Scholar

Carson, R. C., Kiaii, M. & MacRae, J. M. Urea clearance in dysfunctional catheters is improved by reversing the line position despite increased access recirculation. Am. J. Kidney. Dis. 45(5), 883–890. https://doi.org/10.1053/j.ajkd.2005.01.029 (2005).

Article CAS Google Scholar

Chin, A. I., Sheth, V., Kim, J. & Bang, H. Estimating residual native kidney urea clearance in hemodialysis patients with and without 24-h urine volume. Kidney Med. 1(6), 376–382. https://doi.org/10.1016/j.xkme.2019.08.003 (2019).

Article Google Scholar

Download references

Open access funding provided by The Science, Technology & Innovation Funding Authority (STDF) in cooperation with The Egyptian Knowledge Bank (EKB). This work was partially supported by The Science, Technology & Innovation Funding Authority (STDF) of Egypt, project number IG-34795.

Environment Division, National Institute of Oceanography and Fisheries (NIOF), Kayet Bey, Elanfoushy, Alexandria, Egypt

Safaa Ragab, Amany El Sikaily & Ahmed El Nemr

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

The practical portion was led by Dr. S. Ragab and Dr. A.E.S., they also wrote the original manuscript. Dr. A.E.N. supervised the experimental work and finalized the manuscript and submitted to the Journal.

Correspondence to Ahmed El Nemr.

The authors declare no competing interests.

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.

Reprints and Permissions

Ragab, S., El Sikaily, A. & El Nemr, A. Fabrication of dialysis membrane from cotton Giza 86 cellulose di-acetate prepared using Ac2O and NiCl2 as a new catalyst. Sci Rep 13, 2276 (2023). https://doi.org/10.1038/s41598-023-29528-6

Download citation

Received: 20 November 2022

Accepted: 06 February 2023

Published: 08 February 2023

DOI: https://doi.org/10.1038/s41598-023-29528-6

Anyone you share the following link with will be able to read this content:

Sorry, a shareable link is not currently available for this article.

Provided by the Springer Nature SharedIt content-sharing initiative

By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.